Thorlabs 索雷博 AX72502-E3 锥透镜 AX72502-E3 - 锥透镜，ZnSe，Ø1英寸，增透膜：7.0 - 12.0 µm，0.2° 锥透镜，硒化锌概述光束形状反馈棱镜指南 Common Specifications Substrate Material Zinc Selenidea AR Coating Range 7 - 12 µm Reflectance (per Surface)b Ravg < 1%; Rabs < 2% Transmissionb Tavg > 97%; Tabs > 92% AR Coating Plotc Diameter 1" (25.4 mm) Diameter Tolerance +0.0 / -0.05 mm Apex Rounding Diameter (S1) < 1.0 mm Surface Quality (S1, S2) 60-40 Scratch-Dig Surface Flatness (S2) < λ/2 at 633 nm Surface Deviation (RMS) (S1) < 0.07 µm Surface Roughness (RMS) (S1,S2) < 20 Å Clear Aperture (S1, S2) >Ø22.86 mm Edge Thickness 3.4 mm Center Thickness Tolerance ±0.1 mm Angular Tolerance ±...

分类：

Thorlabs索雷博

货号：

AX72502-E3

Thorlabs 索雷博 AX72502-E3 锥透镜

AX72502-E3 - 锥透镜，ZnSe，Ø1英寸，增透膜：7.0 - 12.0 µm，0.2°

锥透镜，硒化锌

概述
光束形状
反馈
棱镜指南

Common Specifications
Substrate Material	Zinc Selenide^a
AR Coating Range	7 - 12 µm
Reflectance (per Surface)^b	R_avg < 1%; R_abs < 2%
Transmission^b	T_avg > 97%; T_abs > 92%
AR Coating Plot^c
Diameter	1" (25.4 mm)
Diameter Tolerance	+0.0 / -0.05 mm
Apex Rounding Diameter (S1)	< 1.0 mm
Surface Quality (S1, S2)	60-40 Scratch-Dig
Surface Flatness (S2)	< λ/2 at 633 nm
Surface Deviation (RMS) (S1)	< 0.07 µm
Surface Roughness (RMS) (S1,S2)	< 20 Å
Clear Aperture (S1, S2)	>Ø22.86 mm
Edge Thickness	3.4 mm
Center Thickness Tolerance	±0.1 mm
Angular Tolerance	±0.01°

点击链接查看基底详细规格
0° AOI时的增透膜范围内
镀膜数据在这里获取

Axicons Selection Guide
UV Fused Silica Axicons	Unmounted
UV Fused Silica Axicons	Mounted
ZnSe Axicons	Unmounted

Click to Enlarge
上图展示了在此页面提到的厚度及角度定义。

特性

将准直光束转换为环形光束
可选五种底角：0.1°、0.2°、0.5°、1.0°和2.0°
宽带增透膜，7到12 µm内R_avg < 1%

锥透镜通常也被称为旋转对称棱镜，是由一个圆锥面和一个平面组成的透镜。锥透镜常用来生成贝塞尔强度分布的光束或锥形非发散光束。将准直光束变为环形光束时，锥透镜的平面应面向准直光源。

这些经过精密抛光的锥透镜的底角范围从0.1°到20°。它们由硒化锌(ZnSe)精密制成，非常适合中红外激光应用或与CO₂激光应用(如材料加工)一起使用。ZnSe锥透镜可选7到12 µm范围的-E3增透膜。增透膜镀在光学元件的两侧，通过降低表面反射率来提高透过率。此外，ZnSe锥透镜在可见光区域提供足够透过率，因此可使用红光对准光束，如HeNe激光器。

锥透镜折射光时遵循斯涅尔定律。可以用来测量偏转角：